Dust suppression method and composition

ABSTRACT

The dissemination of fugitive dust particles into the atmosphere is reduced by treating the particles with an aqueous solution of octylphenoxy polyethoxy ethanol and copolymer of ethylene oxide and propylene oxide.

DISCLOSURE OF THE INVENTION

The present invention relates to a method and composition for preventingthe dissemination of fugitive dust particles into the atmosphere andparticularly to such particles which are hazardous to the environmentand/or personal health and safety.

Indeed, the presence of airborne particulate matter poses a serioushazard with respect to both the environment in general and personalhealth and safety in particular. For example, wind errosion of minetailings has seriously disrupted normal living in the vicinity of mininglocalities. This dust contaminates food, potable water sources andfertile soils and, in some instances, interferes with the driving ofautomobiles on adjacent highways. In addition, airborne particles fromany given source are often inhaled, resulting in serious respiratoryailments such as silicosis.

Common industrial sources of such fugitive dust have been categorized asopen operations, leaks and spills, storage and disposal, an incompletelycontrolled point and poor housekeeping. The iron and steel industriesare replete with examples of these enumerated categories. For example,in the recent past, a well known steel mill was ordered by a court toinstall a system to control the dust, smoke and sparks from itselectrical furnace shop. These fugitive particles emanated from whatwould best be categorized as the "open operations" source noted above.The above-noted disposal and storage source of fugitive dust isexemplified by the facts surrounding the use of a steel mill open hearthprecipitater which has an electrostatic precipitator to control dustemissions. (These dust emissions would be categorized as the controlledpoint-type noted above.) The dust removed by the electrostaticprecipitator is typically collected in hoppers and periodically dumpedinto essentially closed containers known as "collecting pans". Despitethe fact that connecting hoses are extended between the hopper andcollecting pan, considerable fugitive dust emissions occur duringmaterial transfer. If the electrostatically removed particulate matteris to be used as landfill, severe fugitive dust emissions can occurduring the dumping and natural winds have been observed creating greatdust clouds at the landfill sight. The transportation of particulatesalong conveyor belts and the dumping of the particulates therefrom alsocreate fugitive dust emission problems of the "transportation anddisposal" source type. The "leaks and spills" and "poor housekeeping"sources of fugitive dust emissions are seen to be self-explanatory and,thus, further explanation of these categories is considered unwarranted.

As already noted above, the present invention is related to a method andcomposition for preventing the dissemination of fugitive dust into theatmosphere. There already exist both mechanical and chemical methods forpreventing particulate matter from becoming airborne. In the above-notedsteel mill electrical furnace shop a system of hoods was installed onthe furnace and suction fans pull the exhaust through the roof into onelarge duct of over twenty feet in diameter. The exhaust is blown into abag house where harmful particulates are filtered out. These"mechanical" systems are seen to have the inherent drawbacks of beingcumbersome and extremely expensive. Chemical-type controls have beengenerally limited to two basic types, crusting agents and water types.The water-type controls are aimed at preventing dust particles frombecoming airborne by keeping them wet. A few industries have used awater spray-type control with surface tension reducers to increase thewettability of the particles. Of course, the more easily a particlebecomes wetted, the more effective the treatment is considered to be.

According to the present invention, the wettability of fugitive dustparticles, and thus the prevention of the dissemination of such dust tothe atmosphere, is considerably enhanced by applying thereto aneffective amount for the purpose of an aqueous solution of octylphenoxypolyethoxy ethanol (hereinafter referred to as OPE) and copolymer ofethylene oxide and propylene oxide (hereinafter referred to ascopolymer). It was discovered by the present inventor that the benefitsderived from the combination of the two compounds exceeded the benefitsderived from the use of either compound alone with respect to wettingdust particles and, therefore, reducing fugitive dust loads.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 through 7 are plots of penetration time (a measure of dustwetting ability) vs. the proportion of copolymer in mixtures of theclaimed combination of wetting agents. The drawings show thatcompositions within the scope of this invention possessbetter-than-expected ability to wet dust particles.

DETAILED DESCRIPTION OF THE INVENTION

The copolymer is a block copolymer of ethylene oxide and propyleneoxide. The preparation of the copolymer is well known in the art asevidenced by U.S. Pat. No. 2,674,619 which patent is herein incorporatedby reference. As is quite evident from the test results reported below,a wide molecular weight range of copolymer was tested in combinationwith the OPE with enhanced results with respect to particle wetting. Theupper limit for the molecular weight would accordingly be determinedonly by its solubility in the aqueous solvent. Although a copolymerhaving a molecular weight of about 16,000 was tested, some difficultywas experienced getting it into solution. Accordingly, a molecularweight of about 16,000 could be considered as the upper limit for thecopolymer. The preferred upper limit for the molecular weight is about13,300. U.S. Pat. No. 2,674,619 indicates that when the molecular weightof the propylene oxide portion of the copolymer is less than 900, thecopolymer has low surfactant efficacy. Since the present inventorconsiders the surfactant properties of the copolymer to be important tothe operativeness of the present invention it is his opinion that about1000 could be considered the lower molecular weight limit for thecopolymer. The preferred lower limit is about 1950.

The inventive composition also proved to be effective over a wide rangeof ethylene oxide content in the copolymer. To the best of the presentinventor's knowledge, 10% ethylene oxide in the copolymer is the lowestethylene oxide content (ethoxylation) commercially available. A fugitivedust particle treatment using the 10% ethylene oxide copolymer proved tobe effective, and, therefore, that could be considered the lower limitfor the ethylene oxide content. Likewise, to the best of the presentinventor's knowledge, 80% ethoxylation in the copolymer was the highestavailable and proved to be effective despite some problems with gettingthe copolymer into solution. Accordingly, 80% ethoxylation could beconsidered the upper limit for the ethylene oxide content of thecopolymer. The preferred upper limit is 70% ethoxylation.

The ethanol compound is best described as octylphenoxy polyethoxyethanol (OPE) having the general formula: ##STR1## As can be seen fromthe formula, x represents the number of moles of ethylene oxide in thecompound. As will become evident from the test results reported below, awide range of x values was tested successfully. Since at x = 5 the OPEwas water soluble (values below 5 were not), about 5 moles of ethyleneoxide in the compound is the preferred lower limit. The upper limit forx would be determined by the capability of making the compound. To thebest knowledge of the present inventor 40 moles of ethylene oxide is thehighest content that has been made and/or is comercially available.Accordingly, 40 moles of ethylene oxide in the OPE could be consideredthe upper limit. The inventive composition comprises a combination ofthe OPE and the copolymer in a weight ratio of from about 5/95 to 95/5in aqueous solution. Of course the amount of treatment would depend onthe nature and severity of the problem to be treated. In any event, onthe basis of adding the inventive composition to a known water treatmentsystem such as the above-noted water-spray systems, as little as about0.005% by weight of actives (OPE and copolymer) in the aqueous solutionshould be effective. The preferred lower limit is about 0.01% active,while about 0.05% is considered the most desirable lower limit. About 6%actives by weight could be considered the upper limit for theconcentration of OPE and copolymer in the treatment solution. Becausehigher concentrations present stability problems and become impracticalon a cost basis, about 2% is the preferred upper limit and about 1%actives is considered to be the most desirable upper limit.

The preferred method for applying the inventive composition to the dustparticles is by spraying. For example, a ring of sprays has been used atthe Basic Oxygen Furnace (BOF) of a midwestern steel company. The dust(particulate matter) from the discharge of the furnace was collected byan electrostatic precipitator located at the top of the furnace. Thedust removed by the precipitator was transferred to a silo from which itwas dumped into railroad cars. The ring of sprays was located betweenthe silo and the railroad cars and the dust was dumped through the ring.The ring consisted of six spray nozzles, each having a full cone spraypattern covering about 75 degrees of arc. Together, the nozzles werecapable of providing up to 600 gallons of liquid per hour. Of course thenozzle type and arrangement will vary depending on the particularproblem to be treated. For example, a second company used a series ofconveyor belts to convey up to 9000 tons of particulate matter (dust)per day. At various "transfer points" the dust was dumped from oneconveyor belt to another creating serious fugitive dust problems. Asingle spray nozzle at one of the transfer points proved to besufficient in treating the dust. Since the various nozzle arrangementsare considered clearly within the skill of the art, further detailspertaining thereto are deemed unnecessary. The OPE and copolymer couldof course be fed full strength from separate sources into the water feedof the spray nozzles or they could be premixed and/or prediluted.

EXAMPLE 1

The octylphenoxy polyethoxy ethanol component of the inventivecomposition is well known in the art as is the preparation thereof. Onemethod for preparing it is disclosed in the literature as follows:

There are added to a reaction vessel 412 parts of octylphenol and twoparts of sodium hydroxide. The system is swept with nitrogen and thereaction mixture is heated to 139° C. at which point ethylene oxide isintroduced. A total of 817.1 parts of ethylene oxide is added over aperiod of five and one-half hours while the temperature is held at 170°to 185° C. the ethanol compound formed has the formula: ##STR2##

In Examples 2-8 which are reported below, the inventive composition wastested for relative dust wetting activity. As already stated above, themore easily a particle becomes wetted, the more effective a fugitivedust treatment is considered to be. Thus, the test evaluated theeffectiveness of a given treatment by how rapidly (easily) it wets thedust.

Samples of fugitive dust were obtained from various industrial sources.A small portion of each dust sample (1/2 gram) was placed on adepression plate and leveled with a spatula. A drop of the treatmentsolution was placed on the sample and the time required to penetrateinto the dust was measured. The penetration times were found to bereproducible within 15%. Since penetration becomes more difficult as theparticle size decreases a small particle size of -400 mesh was selectedfor purposes of this evaluation. Also, the results obtained in thesetests were found to correlate well with actual field trials. That is,efficacy of a treatment in the field was predictable from these testresults.

EXAMPLE 2

The industrial dust sample utilized in this test was sinter dust. Ofcourse, sintering in the steel industry is a process in whichiron-bearing materials of a fine particle size are converted into courseagglomerates by partial fusion. The treatment composition was an aqueoussolution of OPE having 5 moles of ethoxylation and copolymer having amolecular weight of 2200 and 20% ethoxylation. The aqueous solutioncontained 1% total actives by weight. The results are considered to beself-explanatory and are reported below in Table 1 and in FIG. 1 of theaccompanying drawings in terms of penetration time vs. composition.

                  TABLE 1                                                         ______________________________________                                        Copolymer: MW=2200                                                            20% ethoxylation  OPE: 5 moles ethoxylation                                   Ratio OPE/Copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             56                                                           95/5             52                                                           75/25            47                                                           50/50            26                                                           25/75            10                                                           5/95             73                                                           0/100            330                                                         ______________________________________                                    

To assist the artisan in interpreting these results, the presentinventor's interpretation thereof is presented in the graph in FIG. 1which contains a plot of penetration time vs. treatment composition. Thephantom line is a straight line drawn between the end points representedby OPE alone and copolymer alone. In the absence of enhanced results,the various combinations of OPE and copolymer should yield resultswhich, when plotted, should approximate this straight line. The circledpoints in the graph represent the actual results (shown in Table 1)obtained from the various compositions. The area between the solidcurved line, drawn approximately through these circled points, and thephantom line demonstrates the difference between the predicted resultsand those actually observed. The difference is considered to representenhanced and unexpected results.

EXAMPLE 3

The industrial dust sample utilized in this test was -400 mesh sinterdust. The treatment composition was a 1% (total actives by weight)aqueous solution of OPE having 7.5 moles of ethoxylation and copolymerhaving a molecular weight of 13,300 and 70% ethoxylation. The resultsare reported in Table 2 below and in FIG. 2 of the accompanying drawingsalso in terms of penetration time vs. composition.

                  TABLE 2                                                         ______________________________________                                        Copolymer: MW=13,300                                                          70% ethoxylation  OPE: 7.5 moles ethoxylation                                 Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             75                                                           95/5             71                                                           75/25            69                                                           50/50            80                                                           5/95             196                                                          0/100            620                                                         ______________________________________                                    

As can be seen from Table 2, particularly in conjunction with the graphin FIG. 2, the combination of the copolymer and OPE unexpectedlyenhanced the dust wetting efficacy as compared to that of eithercomponent considered alone.

EXAMPLE 4

The dust utilized in this test was also -400 mesh sinter. The treatmentcomposition was a 1% (total actives by weight) aqueous solution of OPEhaving 10 moles of ethoxylation and copolymer having a molecular weightof 2900 and 40% ethoxylation. The results are reported in Table 3 belowand accompanying FIG. 3 in terms of penetration time vs. composition.

                  TABLE 3                                                         ______________________________________                                        Copolymer: MW=2900                                                            40% ethoxylation  OPE: 10 moles ethoxylation                                  Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             18                                                           95/5             16                                                           75/25            16                                                           50/50            7                                                            25/75            6                                                            5/95             6                                                            0/100            22                                                          ______________________________________                                    

EXAMPLE 5

The treatment composition was treated on -400 mesh sinter dust and was a1% (total actives by weight) aqueous solution of OPE having 12.5 molesof ethoxylation and copolymer having a molecular weight of 6900 and 70%ethoxylation. The results are reported in Table 4 below and in FIG. 4.

                  TABLE 4                                                         ______________________________________                                        Copolymer: MW=6900                                                            70% ethoxylation OPE: 12.5 moles ethoxylation                                 Ratio OPE/copolymer                                                                            Penetration time (seconds)                                   ______________________________________                                        100/0            85                                                            95/5            66                                                            75/25           60                                                            50/50           153                                                           25/75           200                                                           5/95            275                                                           0/100           385                                                          ______________________________________                                    

EXAMPLE 6

A 1% (total actives by weight) aqueous solution of OPE having 16 molesof ethoxylation and copolymer having a molecular weight of 2500 and 30%ethoxylation was tested on -400 mesh sinter dust. The results of thetest are reported in Table 5 below and in FIG. 5. It can be seen fromthese results that the combination of the copolymer and OPE demonstratedenhanced results with respect to wetting the test dust.

                  TABLE 5                                                         ______________________________________                                        Copolymer: MW=2500                                                            30% ethoxylation  OPE: 16 moles ethoxylation                                  Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0            24                                                            95/5            20                                                            75/25           18                                                            50/50           11                                                            25/75           12                                                            5/95            100                                                           0/100           105                                                          ______________________________________                                    

EXAMPLE 7

In this test a 1% aqueous solution of OPE having 30 moles ethoxylationand copolymer having a molecular weight of 4500 and 50% ethoxylation wasapplied to -325/+400 mesh sinter dust. The results of this test arereported below in Table 6 and in the graph in FIG. 6.

                  TABLE 6                                                         ______________________________________                                        Copolymer: MW=4500                                                            50% ethoxylation OPE: 30 moles ethoxylation                                   Ratio OPE/copolymer                                                                            Penetration time (seconds)                                   ______________________________________                                        100/0            650                                                           95/5            470                                                           75/25           320                                                           50/50           315                                                           25/75           235                                                           5/95            275                                                           0/100           370                                                          ______________________________________                                    

EXAMPLE 8

In this test a 1% aqueous solution of OPE having 40 moles ethoxylationand copolymer having a molecular weight of 2200 and 20% ethoxylation wastested on -400 mesh sinter dust. The results are reported in Table 7below and in FIG. 7.

                  TABLE 7                                                         ______________________________________                                        Copolymer: MW=2200                                                            20% ethoxylation OPE: 40 moles ethoxylation                                   Ratio OPE/copolymer                                                                            Penetration time (seconds)                                   ______________________________________                                        100/0            515                                                           95/5            435                                                           75/25           319                                                           50/50           132                                                           25/75           209                                                           5/95            270                                                           0/100           330                                                          ______________________________________                                    

As noted above, the results of the above-reported tests (the results ofwhich are expressed in penetration times) were found to correlate wellwith actual field trials. Although some of the penetration times arerather long, it should be kept in mind that the reported times aremerely relative in that they point out the enhanced wetting abilities ofthe combination of the copolymer and OPE as compared to the componentsalone. While the difference in penetration times between the componentsalone and the combinations correlate with comparative dust particlewetting efficacies the individual penetration times considered alonebear no direct relationship to the wetting of the dust particles forpurposes of this disclosure.

EXAMPLE 9

In Examples 2-8 above, the inventive composition was tested as a 1%solution. To demonstrate its efficacy over a broader range ofconcentrations, the composition was tested as 0.05%, 0.1%, 2% and 6%aqueous solutions. The results are reported in Tables 8-11 below. Thedust was -400 mesh sinter dust. The OPE component of the compositiontested had 16 moles of ethoxylation and the copolymer thereof had amolecular weight of 2500 and 30% ethoxylation (same composition asreported in Example 6 above).

                  TABLE 8                                                         ______________________________________                                        0.05% Aqueous Solution                                                        Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             1255                                                         75/25            893                                                          50/50            762                                                          25/75            950                                                          0/100            1130                                                        ______________________________________                                    

                  TABLE 9                                                         ______________________________________                                        0.1% Aqueous Solution                                                         Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             845                                                          75/25            534                                                          50/50            496                                                          25/75            752                                                          0/100            956                                                         ______________________________________                                    

                  TABLE 10                                                        ______________________________________                                        2% Aqueous Solution                                                           Ratio OPE/copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             4.8                                                          75/25            2.1                                                          50/50            2.5                                                          25/75            1.9                                                          0/100            3.6                                                         ______________________________________                                    

                  TABLE 11                                                        ______________________________________                                        6% Aqueous Solution                                                           Ratio OPE/Copolymer                                                                             Penetration time (seconds)                                  ______________________________________                                        100/0             3.9                                                          75/25            3.6                                                          50/50            2.6                                                          25/75            3.2                                                          0/100            3.4                                                         ______________________________________                                    

Although it would appear from the test results of Table 11 that thebenefits of the inventive composition are uncertain, as noted above atthat concentration significant stability and cost problems exist.

EXAMPLE 10

In Example 4 above, the octylphenoxy polyethoxy ethanol component of theinventive composition had 10 moles of ethoxylation and was tested incombination with copolymer having a molecular weight of 2900 and 40%ethoxylation. In Table 12 below the results are reported for varioustests in which the OPE component described in Example 4 was combinedwith copolymers of ethylene oxide and propylene oxide having differentmolecular weights and degrees of ethoxylation. The solutions tested were1% aqueous solutions and the test dust was -400 mesh sinter dust.

Even though the same OPE was used and the copolymers were varied, it canbe seen from the results in Table 12 that enhanced results were stilldemonstrated with respect to relative dust particle wetting.

    __________________________________________________________________________    Copolymer tested in combination with same OPE having                          10 moles of ethoxylation                                                      Molecular Weight                                                                       Degree of Ethoxylation                                                                    OPE = PENETRATION TIMES (Seconds)                        of Copolymer                                                                           (%)         Copolymer                                                                           100/0                                                                             95/5                                                                             75/25                                                                             50/50                                                                             25/75                                                                             5/95                                                                             0/100                        __________________________________________________________________________    2200     20                18  15 17  19   82  89                                                                              330                          2500     30                18  17 13  17   75  93                                                                              105                          6900     70                18  16 23  109 169 185                                                                              385                          13,300   70                18  12 19  113 143 200                                                                              620                          16,200   80                18  17 23  28  115 205                                                                              385                          4500     50                18  16 18  41   84 114                                                                              370                          __________________________________________________________________________

EXAMPLE 11

The preceding examples are seen to demonstrate that, as relates to dustparticles, the addition of the copolymer component of the inventivecomposition to the OPE component unexpectedly enhances the wettingproperties of the latter component. This discovery was field tested inan industrial steel mill where the dust from the discharge of the BOFfurnace at the mill was collected by an electrostatic precipitatorlocated at the top of the furnace. The dust removed by the precipitatorwas transferred to a silo from which it was dumped into railroad cars.It was at this dumping site that fugitive dust loading was observed inamounts of 15-16 mg. dust/ft³. In an effort to reduce this dust load, aring of spray nozzles was located between the silo and the railroad carand the dust was dumped through the ring as water was sprayed on thedust from the nozzles. The ring consisted of six nozzles each having afull cone spray pattern covering about 75 degrees of arc. The dust loadswere measured using a high volume sampler which was placed about 15 feetabove the top of the railroad car and was operated 3-5 minutes at 50standard cubic feet per minute (scfm) while the silo was being unloaded.Fifty tons of dust were dumped through the spray ring in 50 minutes. Thewater pressure was varied between 0-35 pound per square inch (psi) andthe water volume was varied between 0-600 gallons per hour (gph). Thetest results are reported below in Table 13 in terms of dust load(concentration of fugitive dust). The inventive composition (Product A)consisted of the following:

Ethylene glycol; 3%

Ope; 15%

copolymer; 5%

Water; 77%

The OPE had 10 moles of ethoxylation and the copolymer had a molecularweight of 1950 and 10% ethoxylation. The ethylene glycol was used merelyas a solution stabilizer for purposes of long term product stability.The treatment was added by supplying an aqueous solution of theOPE/copolymer to a water supply line to the nozzles. For comparison, thefugitive dust was also treated with water alone and a 0.264% aqueoussolution of the OPE alone having 10 moles of ethoxylation (Product X).

                  TABLE 13                                                        ______________________________________                                        Product A: Inventive Composition, 0.2% actives                                Product X: OPE component tested alone                                                 Water Pressure                                                                            Concentration of Fugitive Dust                            Treatment                                                                             (psi)       (mg/ft.sup.3)                                             ______________________________________                                        Water   5           14                                                        Product X                                                                             5           8                                                         Product A                                                                             5           1.5                                                       Water   10          8                                                         Product X                                                                             10          3                                                         Product A                                                                             10          less than 1                                               ______________________________________                                    

From these results it can be seen that the addition of the copolymer tothe OPE component ehance the fugitive dust control properties of theOPE, as was predicted from the test results of the preceding examples.

EXAMPLE 12

The inventive composition described in Example 11 was field tested inthe sinter cooler area of a second steel mill. The sinter dust was beingdumped from the cooler into a dumping car. It was at this dumping sitethat high levels of fugitive dust were observed. Three spray nozzleswere located beneath the cooler and sprayed into the dumping car in anattempt to alleviate this dust problem. Each nozzle produced a spraypattern covering about 180° of arc. A high volume sampler was again usedto measure the dust loads. For comparison, the dust was treated withwater alone and first and second aqueous solutions of the OPE having 10moles of ethoxylation. The first aqueous solution, Product Y, contained0.09% OPE; and the second, Product Z, contained 0.26% of the same. Theresults are reported in Table 14 below in terms of concentration ofdust. The water pressures reported are those for the water supplied tothe nozzles.

                  TABLE 14                                                        ______________________________________                                        Product A: Inventive Composition, 0.2% actives                                Product Y: 0.09% Aqueous Solution of OPE                                      Product Z: 0.26% Aqueous Solution of OPE                                              Water Pressure                                                                            Concentration of Fugitive Dust                            Treatment                                                                             (psi)       (mg/ft.sup.3)                                             ______________________________________                                        Water   10          7.5                                                       Product Y                                                                             10          3.2                                                       Product Z                                                                             10          2.9                                                       Product A                                                                             10          2.3                                                       Water   50          2.2                                                       Product Y                                                                             50          1.9                                                       Product X                                                                             50          1.5                                                       Product A                                                                             50          less than 1                                               ______________________________________                                    

Having thus described my invention, I claim:
 1. A method for enhancingthe reduction of the dissemination of fugitive dust particles into theatmosphere comprising: treating the dust particles with an effectiveamount for the purpose of an aqueous solution of octylphenoxy polyethoxyethanol and copolymer of ethylene oxide and propylene oxide, wherein theweight ratio of the ethanol compound to the copolymer is from about 5/95to 95/5, wherein the copolymer has a molecular weight of from about 1000to 16,000 and an ethylene oxide content of from about 10% to 80%,wherein the ethanol compound has from about 5 to 40 moles of ethyleneoxide, and wherein the total concentration of the ethanol compound andthe copolymer in the aqueous solution is from about 0.005% to 6%.
 2. Themethod of claim 1, wherein the treatment is applied by spraying.
 3. Themethod of claim 2, wherein the treatment also consists essentially of aneffective amount for the purpose of a solution stabilizer.
 4. The methodof claim 3, wherein the stabilizer is ethylene glycol.
 5. The method ofclaim 2, wherein the fugitive dust particles are discharged from a basicoxygen furnace.
 6. The method of claim 4, wherein the fugitive dustparticles are discharged from a basic oxygen furnace.
 7. The method ofclaim 2, wherein the fugitive dust particles are sinter dust.
 8. Themethod of claim 4, wherein the fugitive dust particles are sinter dustparticles.
 9. The method of claim 1, wherein the copolymer has amolecular weight of from about 1950 to 13,300.
 10. The method of claim2, wherein the copolymer has a molecular weight of from about 1950 to13,300.
 11. The method of claim 5, wherein the copolymer has a molecularweight of from about 1950 to 13,300.
 12. The method of claim 7, whereinthe copolymer has a molecular weight of from about 1950 to 13,300. 13.The method of claim 1, wherein the treatment is applied by spraying itonto airborne dust particles.
 14. A composition for enhancement of thereduction of the dissemination of fugitive dust into the atmospherecomprising an aqueous solution of:octylphenoxy polyethoxy ethanol, andcopolymer of ethylene oxide and propylene oxide,wherein the totalconcentration of the ethanol compound and the copolymer in the aqueoussolution is from about 0.005% to 6%, the copolymer has a molecularweight of from about 1000 to 16,000 and an ethylene oxide content offrom about 10% to 80%, the ethanol compound has from about 5 to 40 molesof ethylene oxide, and wherein the weight ratio of the ethanol compoundto the copolymer is from about 5/95 to 95/5.
 15. The composition ofclaim 14, wherein the total concentration of the ethanol compound andthe copolymer in the aqueous solution is from about 0.05 to 2%.
 16. Thecomposition of claim 14, further comprising an effective amount for thepurpose of a solution stabilizer.
 17. The composition of claim 16,wherein the stabilizer is a lower alkylene glycol.
 18. The compositionof claim 17, wherein the stabilizer is ethylene glycol.
 19. Thecomposition of claim 18, wherein the ethanol compound comprises 15% ofthe composition, the copolymer comprises 5% of the composition, theethylene glycol comprises 3% of the composition, and the water comprises77% thereof.
 20. The composition of claim 14, wherein the copolymer hasa molecular weight of from about 1950 to 13,300.
 21. A composition forenhancement of the reduction of the dissemination of fugitive dust intothe atmosphere consisting of an aqueous solution of:octylphenoxypolyethoxy ethanol, copolymer of ethylene oxide and propylene oxide, andsolution stabilizer,wherein the weight ratio of the ethanol compound tothe copolymer is from about 5/95 to 95/5, the copolymer has a molecularweight of from about 1000 to 16,000 and an ethylene oxide content offrom about 10% to 80%, the ethanol compound has from about 5 to 40 molesof ethylene oxide, and wherein the total concentration of the ethanolcompound and the copolymer in the aqueous solution is from about 0.005%to 6%.